9528 Industrial emergency repair agent
Performance characteristics
☆ Fast curing speed;
☆ Low surface treatment requirements, with oil, water construction;
☆ Good bonding strength with all kinds of metals.
Product use
Can be repaired with oil, mainly used for transformers, oil tanks, oil tanks, oil pipes, and other equipment oil leakage repair.
Usage method
1. Surface treatment: rough and clean the surface.
2. Preparation: According to the mass ratio A:B=1:1 or volume ratio A:B=1:1, mix the two components A and B evenly, and use immediately.
3. Coating: Apply the mixed material to the part to be repaired and compacted so that it is fully infiltrated with the base material.
4. Curing: 20 ~ 25℃ curing 20min can be put into use, if the temperature is too low should be heated or extended curing time to cure.
9101 Industrial cast iron repair agent
Packing specification: 500g/ group, 16 groups/box
Two-component, universal type. The physical state is paste, the volume is 303 cm3, the operation time is 25min (25℃), the curing time is 18h (25℃), and it is used for filling various casting.
9111 Industrial iron repair agent
Packing specification: 500g/ group, 16 groups/box
The physical state is paste, the volume is 309cm3, the operation time is 45min (25℃), the curing time is 24h (25℃), the comprehensive mechanical properties are good, especially suitable for gray iron, ductile iron and other materials, for the repair of cast iron, such as casting fill and parts wear, corrosion, rupture repair.
9112 Industrial steel repair agent
Packing specification: 500g/ group, 16 groups/box
The physical state is paste, the volume is 298cm3, the operation time is 45min (25℃), the curing time is 24h (25℃), the wear resistance and bonding strength are high, and it is used for the repair of various carbon steel, alloy steel and stainless steel. Such as casting filling and parts wear, scratches, corrosion, rupture repair.
9113 Industrial aluminum repair agent
Packing specification: 250g/ group, 16 groups/box
The physical state is paste, the volume is 177cm, the operation time is 45min (25℃), the curing time is 24h (25℃), and it is used for the repair of various cast aluminum parts and the repair of aluminum parts wear.
9114 Industrial copper repair agent
Packing specification: 250g/ group, 16 groups/box
The physical state is paste, the volume is 163 cm3, the operation time is 45min (25℃), the curing time is 24h (25℃), it is used for the repair of brass, bronze castings and process casting parts.