Two components ,It is made up of all kinds of high performance wear resisting ,corrosion resistant material or antifriction material (such as ceramic ,silicone carbide ,titanium alloys,molybdenum disulfide etc.) and modified composite toughening heat-resistance resin to get a high performance wear resisting corrosion polymerization ceramic material . It can be widely used in all kinds of wear parts repair and all kinds of wear resistance anti corrosion for organic surface preparation anticorrosive coating .

Features 

l   anti corrosion is  2times  as normal metal 

l   have high sticking strength with basic material of metal 

l   easy to operate , no need of the high technical requirement for operation personnel .

l   suitable for repair and protection to all kinds of corrosion condition .

215 Anti-wear Repair Agent Adhesive 

Packaging Spec.：500g/set、16sets/carton 

 Physical statues is paste .Volume is 325cm³. Operation time limit is (25℃) 45mins.  it can be used for (25℃) 24h.It can accurately fix the friction and wear failure of the shaft neck,shaft hole, bearing and other parts .

216 Anti-wear Repair Agent Adhesive 

Packaging Spec.：500g/set、16sets/carton 

Physical statues is paste-like .Volume is 240cm³. Operation time limit is (25℃) 45mins.  it can be used for (25℃) 24h.It can be used for general loading fine particle erosion and wearing of the pump body ,impeller,fan shell ,repair of the pipe screw conveyor,etc and its protection.

218 Anti-wear Repair Agent Adhesive 

Packaging Spec.:500g/set、16sets/carton

Physical status is paste ,volume is 305cm³，operatoin time limit is (25℃) 45min, it can be used for (25℃) 24h. It is used for coarse particle erosion and wear of the pump body ,transporting tank,high sand content condition with the water pump ,repair of the pipe bend ,etc and its protection.

                                                                            Technical Data Sheet 

Usage Method 

l     surface treatment:make the need repair surface rough , make the surface have 1.5mm deep thread and then clean with cleaning agent 

l     Mixing: mix A with B according to the proportion

 on the instruction and finish it within the specified operating period .

l     Coating: apply the mixed coating layer by layer on the repair part.The first layer should be compacted,fully infiltrated with the base material . If the following needs mechanical processing ,leave appropriate machining allowance.

l     Curing: the temperature is from 25 to 30 degrees. After 8 hours curing , it can undertake mechanical processing and can be put into use after 24 hours. If the temperature is low ,please heat them or keep longer time for curing .