801 Rubber adhesive
Performance characteristics
☆ Good toughness, wear resistance, impact resistance;
☆ High bonding strength, good insulation;
☆ Can be cured at room temperature, easy to use.

Product use
Good toughness, high bonding strength. Used for self-adhesive and cross-adhesive between transport belt, rubber, leather, metal, ceramic and other materials. The peeling strength of the adhesive part is better than the bonding strength between ordinary conveyor belt rubber and fabric.
Usage method
1. Surface treatment: Hair the area to be repaired, clean and decontaminate, and dry.
2. Preparation: Pour the curing agent group B into the main agent group A in the tin can quickly stir evenly, and then pour to the place to be repaired and smooth.
3. Curing: normal temperature curing 8 hours can be used, 24 hours to reach strength.
Performance parameter

Special instructions
1. This parameter is obtained under laboratory conditions. Due to the complexity of the actual working conditions, it is recommended that users do pre-test according to the actual working conditions.
2. The rubber layer cannot be stressed when it is not cured (within 2 hours);
3. If the temperature is too low, the viscosity of A and B components is large, and the A and B components can be heated to about 30 ° C before use and then mixed.
Storage: Sealed storage in a cool and dry place, shelf life of 9 months.
Packaging specifications: Two components, flame retardant type, 1000g/ set, 10 sets/box.

 
 
916 Rubber repair agent
Performance characteristics
☆ Fast curing speed, good adhesion, high strength;
☆ Wear resistance, good filling;
☆ Medium resistant, aging resistant, easy to operate.

Product use
It is used for splicing repair of longitudinal and transverse tear of steel core, whole core and ordinary conveyor belt, as well as conveyor belt surface wear, falling block, belt edge wear, belt surface perforation and joint sealing; Repair of cables, rollers and other rubber products.
Usage method
1. Surface treatment: Hair the area to be repaired, clean and decontaminate, and dry.
2. Brush treatment agent: Brush treatment agent (group C) on the roughed part to be repaired and let dry. When conditions permit, bake with tungsten iodide lamp for 10-15 minutes until the surface to be repaired reaches 60℃.
3. Preparation: Pour the curing agent group B into the main agent group A in the tin can quickly stir evenly, and then pour to the place to be repaired and smooth.
4. Curing: normal temperature curing 4-6 hours can be used, 48 hours to reach strength.
Performance parameter

Special instructions
1. This parameter is obtained under laboratory conditions. Due to the complexity of the actual working conditions, it is recommended that users do pre-test according to the actual working conditions.
2. The product should be controlled within 8 minutes from mixing to using up, and the adhesive layer cannot be stressed when it is not cured (within 2 hours);
3. If the temperature is too low, the viscosity of A and B components is large, and the A and B components can be heated to about 30 ° C before use and then mixed.
Storage: Sealed storage in a cool and dry place, shelf life of 9 months.
Packing specification: three components, brushable, 300g/ set, 16 sets/box.