Polymetallic repair
It is a high-performance polymeric metal material obtained by composite of a variety of alloy materials and modified toughened and heat-resistant resins. It is widely used in various casting parts after repair, the color is basically the same as the base material, has high strength, and can be processed with the base material.
Product characteristics
The cured material has a high strength and can be processed by various machines
High bonding strength with metal
The repaired color is basically the same as the base material
Wide range of applications, suitable for all kinds of metal material repair
It has abrasion resistance, corrosion resistance and aging resistance
101 Casting repair agent
Packing specification: 500g/ group, 16 groups/box
Two-component, universal type. The physical state is paste, the volume is 303 cm3, the operation time is 25min (25℃), the curing time is 18h (25℃), and it is used for filling various casting.
102 Casting repair agent
Packing specification: 250g/ group, 16 groups/box
Two-component, universal type. Physical state is paste, operation time (25℃) 65min, curing time (25℃)24h, fluid shape, used to repair defects less than 2mm.
111 iron repair agent
Packing specification: 500g/ group, 16 groups/box
The physical state is paste, the volume is 309cm3, the operation time is 45min (25℃), the curing time is 24h (25℃), the comprehensive mechanical properties are good, especially suitable for gray iron, ductile iron and other materials, for the repair of cast iron, such as casting fill and parts wear, corrosion, rupture repair.
112 Steel repair agent
Packing specification: 500g/ group, 16 groups/box
The physical state is paste, the volume is 298cm3, the operation time is 45min (25℃), the curing time is 24h (25℃), the wear resistance and bonding strength are high, and it is used for the repair of various carbon steel, alloy steel and stainless steel. Such as casting filling and parts wear, scratches, corrosion, rupture repair.
113 Aluminum repair agent
Packing specification: 250g/ group, 16 groups/box
The physical state is paste, the volume is 177cm3, the operation time is 45min (25℃), the curing time is 24h (25℃), and it is used for the repair of various cast aluminum parts and the repair of aluminum parts wear.
114 Copper repair agent
Packing specification: 250g/ group, 16 groups/box
The physical state is paste, the volume is 163 cm3, the operation time is 45min (25℃), the curing time is 24h (25℃), it is used for the repair of brass, bronze castings and process casting parts.
2111 Super Metal repair
Packing specification: 500g/ group, 16 groups/box
The physical state is paste, the operation time is 70min (25℃), the curing time is 24h (25℃), the high strength type, the comprehensive mechanical properties are good, used to repair all kinds of metal defects.
| Metal repair agent (main physical and mechanical properties) | |||||||
| Performance name | FS/101 | FS/102 | FS/111 | FS/112 | FS/113 | FS/114 | FS/2111 |
| colour | grey | grey | grey | grey | grey | grey | friends |
| Mixing ratio | 2:1 | 2:1 | 7:1 | 7:1 | 6:1 | 6:1 | 7:1 |
| Operating time (25℃,min) | 65 | 65 | 65 | 65 | 60 | 80 | 70 |
| Initial setting time (25℃, H) | 4 | 4 | 4 | 4 | 4 | 5 | 4.5 |
| Full set time (25℃, H) | 24 | 24 | 24 | 24 | 24 | 24 | 24 |
| Shear strength (Mpa, GB/T7214) | 20.0 | 20.0 | 20.0 | 19.0 | 22.0 | 20.0 | 21.0 |
| Compressive strength (Mpa,GB/T1041) | 95.0 | 95.0 | 110.0 | 99.5 | 105.0 | 107.0 | 165.0 |
| Hardness (Shore D, GB/T 2411) | 80 | 80 | 82 | 82 | 81 | 82 | 85 |
| Operating temperature (℃) | - 60 ~ + 120 | -60~ +150 | |||||
| Packing specification | 250g/ set | 250g/ set | 500g/ set | 500g/ set | 250g/ set | 250g/ set | 500g/ set |
Usage method
Surface treatment: The surface is roughened and cleaned with a cleaning agent.
l Preparation: According to the proportion of the product description, the two components A and B are mixed evenly, and used up within the specified operating period.
Coating: Apply the mixed material layer by layer on the part to be repaired, one layer should be compacted, so that it is fully infiltrated with the substrate. If mechanical processing is required in the following sequence, an appropriate amount of processing allowance should be set aside.
Curing: 25 ~ 30℃ curing for 8 hours can be machined, put into use after 24 hours, if the temperature is low should be heated or extended curing time to cure.