High temperature metal repair agent
Model: 9001.9002.9011.9012.9013.9014.9015.916.918.926.928
Brand: Feng Shen
High temperature metal repair agent series
Product features:
High bonding strength with metal.
Curable at room temperature.
The appearance is consistent with that of the base material to be repaired.
Product description
FS9001 high temperature defect repair agent
Packing specification: 500g/ group mass ratio: 1:1
Physical state, paste, operation time (25℃)100min, curing time (25℃)24h, used to repair pores, sand holes, cracks and other defects under high temperature conditions.
FS9002 High temperature liquid iron repair agent
Packing size: 500g/ group
Mass ratio: 2:1
Physical state, liquid, operating time (25℃)100min, curing time (25℃)24h, low viscosity, with fluidity, used to repair the defects of less than 2mm under high temperature conditions.
FS9011 high temperature iron repair agent
Packing size: 500g/ group
Mass ratio: 6:1
Physical state, cement, operating time (25℃)100min, curing time (25℃)24h, for high temperature conditions of cast iron holes, sand holes, cracks and other defects repair.
FS9012 high temperature steel repair agent
Packing size: 500g/ group
Mass ratio: 6:1
Physical state, paste, operation time (25℃)100min, curing time (25℃)24h, for high temperature conditions under the repair of steel casting defects, such as wear, scratches, corrosion.
FS9014 high temperature copper repair agent
Packing size: 500g/ group
Mass ratio: 5:1
Physical state, paste, operation time (25℃)95min, curing time (25℃)24h, temperature resistance 250℃, color and copper parts are basically the same, used for a variety of brass, bronze parts of the defect repair.
FS916 high temperature wear resistant repair agent
Packing size: 500g/ group
Mass ratio: 4:1
The physical state is paste, the operation time is 100min (25℃), the curing time is 24h (25℃), which is used to repair the local wear of the equipment under the condition of dust particles and abrades in high temperature environment.
FS926 high temperature wear resistant coating
Packing size: 2kg/ group
Mass ratio: 2:1
The physical state is paste, the operation time is 100min (25℃), the curing time is 24h (25℃), which is used to repair the large area wear of the equipment under the condition of fine particle impact at high temperature environment or make protective coating.
FS9013 high temperature aluminum repair agent
Packing size: 500g/ group
Mass ratio: 5:1
The physical state is paste, the operation time is 95min (25℃), the curing time is 24h (25℃), and the temperature is 250℃. It is used for the repair of various aluminum and aluminum alloy defects.
FS915 high temperature titanium wear resistant adhesive
Packing size: 500g/ group
Mass ratio: 5:1
Physical state, paste, operation time (25℃)100min, curing time (25℃)24h, good wear resistance, used to repair worn shaft, shaft hole, spline, keyway.
FS918 high temperature wear resistant repair agent
Packing size: 500g/ group
Mass ratio: 4:1
The physical state is paste, the operation time is 100min (25℃), the curing time is 24h (25℃), and it is used to repair the local wear of the equipment under the condition of coarse-grained abrasive in high temperature environment.
FS928 high temperature wear resistant coating
Packing size: 2kg/ group
Mass ratio: 1:1
The physical state is paste, the operation time is 100min (25℃), the curing time is 24h (25℃), and it is used to repair the large area wear of the equipment under the coarse particle impact condition in high temperature environment or make protective coating.
| High temperature metal/wear resistant repair agent (main physical and mechanical properties) | |||||||||||
| Performance name | FS/9001 | FS/9002 | FS/9011 | FS/9012 | FS/9013 | FS/9014 | FS/915 | FS/916 | FS/918 | FS/926 | FS/928 |
| colour | grey | grey | Cast iron | steel | aluminum | copper | black | grey | grey | grey | grey |
| Mixing ratio | 1:01 | 2:1 | 6:1 | 6:1 | 5:1 | 5:1 | 5:1 | 4:1 | 4:1 | 2:1 | 1:01 |
| Operating time (25℃,min) | 100 | 100 | 100 | 100 | 95 | 95 | 100 | 100 | 100 | 100 | 100 |
| Initial setting time (25℃, h) | 6 | 6 | 6 | 6 | 6 | 6 | 6 | 6 | 6 | 6 | 6 |
| Full set time (25℃, h) | 24 | 24 | 24 | 24 | 24 | 24 | 24 | 24 | 24 | 24 | 24 |
| Shear strength (Mpa, GB/T 7214) | 22.0 | 22.0 | 22.0 | 22.0 | 21.0 | 20.0 | 19.0 | 14.0 | 9.0 | 8.0 | 6.5 |
| Compressive strength (Mpa,GB/T 1041) | 100.0 | 102.0 | 95.0 | 110.0 | 115.0 | 113.0 | 130.0 | 119.0 | 115.0 | 98.0 | 91.0 |
| Hardness (Shore D, GB/T 2411) | 82 | 82 | 85 | 85 | 84 | 82 | |||||
| Operating temperature (℃) | . - 60-220 + | ||||||||||
| Packing specification | 500g/ set | 10kg/ set | |||||||||
Usage method
Surface treatment: Rough the repaired part, if conditions permit, drive out 1.5mm deep indulge grain, and then clean with cleaning agent.
Preparation: According to the proportion of the instructions, the A and B components are mixed evenly, and used up within the specified operating period.
Coating: The mixed material is coated layer by layer on the part to be repaired, and it should be compacted so that it is fully infiltrated with the substrate. If mechanical processing is required in the following sequence, an appropriate amount of processing allowance should be set aside.
Curing: 25 ~ 30℃ curing for 8 hours can be machined, can be put into use after 24 hours, if the temperature is low should be heated or extended curing time to cure.