FS226 wear resistant coating

Performance characteristics

1. High bonding strength with metal, wood, stone and other substrates;

2. No flow, short molding time, fast curing speed;

3. Suitable for large area repair of fine particle wear equipment and preparation of pre-protective coating.

Product characteristics

The wear-resistant composite coating with hard spherical small particle ceramics and quartz as the aggregate has high bonding strength with a variety of substrates. For large area repair and pre-protection coating of fine particle wear equipment, such as feeders, scrapers, hoppers and chutes.

Usage method

1. Surface treatment: roughening the parts that need to be treated; Clean the roughened surface to achieve no

Oil pollution, no dust;

2. Configuration: Mix A and B components evenly according to the weight ratio 4:1, and use them up within 30 minutes; The curing speed is affected by temperature, and the general amount of glue should not be greater than 1.5 kg;

3. Coating: The thickness of this coating is appropriate in 2 ~ 8mm, the mixed material is divided into two layers coating, one layer and the substrate fully infiltrate and compacted, then apply two layers and smooth until;

4. Curing: It can be put into use for 24 hours under the condition of temperature 25℃. Under the condition of general low temperature, proper heating or extension of curing time can be used to cure.

Storage and shelf life

Non-dangerous goods, sealed storage in a cool and dry place, shelf life of 12 months;

Packing: 10kg/ group, 20kg/ group, plastic drum.